| 品牌：德国赢创德固赛 | 牌号：ZK40 | 特性级别：高抗冲 |
| 用途级别：汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 | 弯曲强度：未知kg/cm2 | 成型收缩率：未知% |
| 阻燃等级：UL 阻燃等级 (1.60 mm)HB | 熔体流动速率：0.700cm3/10ming/10min | 密度：1.13g/cm3g/cm3 |
| 拉伸强度：1600MPakg/cm2 | 断裂伸长率：30%% | 缺口冲击强度：80kJ/m2kg.cm/cm |
| 热变形温度：92.0°C℃ | 可售卖地：全国 |
PLEXIGLAS ZK40 德国赢创德固赛PMMA
Plexiglas Resist zk40聚甲基丙烯酸甲酯-丙烯酸Evonik Industries AG产品说明：Product Profile:
PLEXIGLAS Resist zk40 is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).
Typical properties of impact-modified PLEXIGLAS molding compounds are
excellent transmission and clarity
brilliant appearance
the pleasant feel and sound of the moldings.
PLEXIGLAS Resist zk40 is characterized by the following special properties:
very good break resistance and impact strength
improved resistance to stress cracking
AMECA listing.
Application:
Used for injection molding. Profile extrusion or coextrusion are also possible.
Examples:
lighting fixtures, writing and drawing utensils, domestic appliances and sanitaryware
Plexiglas Resist zk40 物性表
| 基本信息 | |
|---|---|
| 添加剂 | 冲击改性剂
|
| 特性 | 高 ESCR（抗应力开裂） 抗撞击性，高 清晰度，高 外观良好
|
| 用途 | 电器用具 柔软的把手 卫浴产品 文具 型材
|
| 形式 | 粒子
|
| 加工方法 | 共挤出成型 挤出 注射成型
|
化学性能
聚甲基丙烯酸甲酯的单体是甲基丙烯酸甲酯，为无色液体，具有香味，沸点101℃，密度为0.940克/厘米3(25℃）。
工业上是先用法或异丁烯催化氧化法制出甲基丙烯酸，然后酯化而得。它容易聚合,需要在5℃以下存放，或加入0.01%左右的对苯二酚阻聚剂来保存。使用前将其蒸馏，把阻聚剂分出。
聚甲基丙烯酸甲酯能溶于自身单体、氯仿、乙酸、乙酸乙酯、丙酮等有机溶剂。由于它能溶于自身单体中，它的本体
注塑模工艺条件：
干燥处理：PMMA具有吸湿性因此加工前的干燥处理是必须的。建议干燥条件为90C、2~4小时。
熔化温度：240~270C。 模具温度：35~70C。
注射速度：中等
化学和物理特性PMMA具有优良的光学特性及耐气侯变化特性。白光的穿透性高达92%。PMMA制品具有很低的双折射，特别适合制作影碟等。PMMA具有室温蠕变特性。随着负荷加大、时间增长，可导致应力开裂现象。PMMA具有较好的抗冲击特性。
由于PMMA表面硬度不高、易擦毛、抗冲击性能低、成型流动性能差等缺点，PMMA的改性相继出现。如甲基丙烯酸甲酯与苯乙烯、丁二烯的共聚，PMMA与PC的共混等。 超级透明PMMA材料主要用于手机保护屏，该产品分为有硬化涂层，没有硬化涂层两种.其特点是透光率极好，没有杂质，静电保护膜，表面硬化厚后硬度可达5-6H以上.目前特别推荐用于硬化处理的PMMA材料，国内称为生板。